![]() When glass containers break they often seem to violently explode in all directions. Glass usually appears to fracture instantly and dramatically, as when a thrown rock or other projectile hits a glass window. ![]() However, the topographical surface features of the broken glass and the resulting crack patterns of the reconstructed glass object will accurately, objectively, and faithfully document the history of the glass fracture event. Eyewitness accounts are not always reliable as the anxiety of the moment may create confusion among observers. From a more practical perspective, there is the assignment of responsibility for glass failures in litigation when there are personal injuries. It also includes understanding how and why cracks in glass extend or grow in the myriad of ways that they do. Paramount, from an academic point of view, is the continuing quest for a greater fundamental understanding of glass strength. The fracture surface topography and the crack patterns that develop when any glass object breaks are of interest for many reasons. Other glass crack patterns such as those from impact and thermal stress are also considered. The patterns of crack branching or forking, the branching angles and the crack length prior to forking, are also discussed. Characteristic cracking patterns are reviewed for several common glass fractures including those for pressure breaks, both bottle explosions and flat glass window failures from wind pressure whose basic similarities are described. Dicing fragmentation of high-strength tempered glass and the long sword-like shards of low-strength annealed glass fracture are contrasted through their strain energies. Distinctive crack patterns that evolve during fracture, that is the traces of the cracks intersecting the glass free surfaces, are described. Formation of the mist and hackle surface regions are also fundamentally addressed, as is crack branching. The concept of a fracture mirror constant is related to the strength. Quantitative aspects of the fracture process such as the stress level at fracture for a glass object are directly related to the size of the fracture mirror. The surface features known as the mirror, the mist, and the hackle are illustrated and addressed through the principles of fracture mechanics and associated energy criteria. Strength is central to the fracture surface features for it determines the strain energy release rate and the dynamics of crack extension. They are considered after a brief discussion of glass strength. View the Groupon Goods FAQ for additional information, including how list price is determined.The topographical features which appear on the fracture surfaces of broken glass objects and the resulting crack patterns which develop are Nature’s documentation of the fracture event. For post-purchase inquiries, please contact Groupon customer service. How to get your goods: by purchasing this Groupon and providing your name and shipping address, your order is complete!įor questions pertaining to this deal, please visit the deal Q&A on this page. Editing tools for orientation, cropping, borders, or applying greyscale.Multiple sizes in landscape, portrait, and square orientations. ![]()
0 Comments
Leave a Reply. |
AuthorWrite something about yourself. No need to be fancy, just an overview. ArchivesCategories |